[交流]
求助關(guān)于EIS的審稿人意見 已有1人參與
|
|||
|
在關(guān)于不銹鋼表面鈍化膜EIS表征方面遇到審稿人的問題,不知道我理解的有沒有問題,向大神們求助。Performing EIS measurement after 10 min or 40 min is not really relevant. We need to have stationarity of the system to characterize correctly the passive layer. Authors show that the potential still evolve during the EIS measurement and consequently the results they show is different from the first version but it is still not accurate. - Consequently, The EEC used is not suitable and the parameters obtained for EIS diagram interpretation need to be studied with more attention. The physical meaning of this parameters must be the guidelines for a good understanding of the interface behavior and reactivity. 審稿人覺得我擬合的阻抗數(shù)據(jù)跟他的經(jīng)驗(yàn)不符,數(shù)量級(jí)上差半個(gè),覺得我的系統(tǒng)不夠穩(wěn)定造成的,我是用R(RQ)(RQ)模型擬合的結(jié)果,他覺得這個(gè)也有問題。 但是我做實(shí)驗(yàn)的時(shí)候ocp確實(shí)已經(jīng)比較穩(wěn)定了,而且擬合結(jié)果也挺好的,所以我打算再做長(zhǎng)時(shí)間的靜置,再測(cè)eis,再用R(Q(R(RQ)))擬合試試,確實(shí)對(duì)界面行為理解沒那么透徹,不知道我對(duì)他的意見領(lǐng)會(huì)的對(duì)不對(duì),請(qǐng)各位指點(diǎn)啊,小弟金幣不足,下次再來(lái)感謝,求求各位大佬。 發(fā)自小木蟲Android客戶端 |

木蟲 (正式寫手)
|
你可以 把你的阻抗做K-K轉(zhuǎn)換 證明你的阻抗是有效的 發(fā)自小木蟲IOS客戶端 |


| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 0703化學(xué)306調(diào)劑 +4 | 26要上岸 2026-03-03 | 4/200 |
|
|---|---|---|---|---|
|
[考研] 理學(xué),工學(xué),農(nóng)學(xué)調(diào)劑,少走彎路,這里歡迎您! +8 | likeihood 2026-03-02 | 11/550 |
|
|
[考研] 264求調(diào)劑 +6 | 26調(diào)劑 2026-03-03 | 6/300 |
|
|
[考研] 0856材料工程,初試313調(diào)劑 +6 | 賣個(gè)關(guān)子吧 2026-03-03 | 6/300 |
|
|
[考研] 環(huán)境調(diào)劑 +5 | 柒槿levana 2026-03-01 | 5/250 |
|
|
[考研] 一志愿華中科技大學(xué),化學(xué)專業(yè)344分,求調(diào)劑 +6 | 邢xing1 2026-03-02 | 6/300 |
|
|
[考研] 調(diào)劑 +5 | 13853210211 2026-03-02 | 7/350 |
|
|
[論文投稿]
通訊作者寫誰(shuí),問題是你意想不到的問題
15+3
|
阿爾法啊 2026-03-01 | 3/150 |
|
|
[考研] 調(diào)劑材料學(xué)碩 +4 | 詞凝Y 2026-03-02 | 4/200 |
|
|
[考研]
|
好好好1233 2026-02-28 | 16/800 |
|
|
[考研] 11408,學(xué)碩276求調(diào)劑 +3 | 崔wj 2026-03-02 | 5/250 |
|
|
[考研] 0856材料求調(diào)劑 +12 | hyf hyf hyf 2026-02-28 | 13/650 |
|
|
[考研] 一志愿山東大學(xué)材料與化工325求調(diào)劑 +5 | 半截的詩(shī)0927 2026-03-02 | 5/250 |
|
|
[考研] 281求調(diào)劑 +5 | 2026計(jì)算機(jī)_誠(chéng)心 2026-03-01 | 8/400 |
|
|
[基金申請(qǐng)] 成果系統(tǒng)訪問量大,請(qǐng)一小時(shí)后再嘗試。---NSFC啥時(shí)候好哦,已經(jīng)兩天這樣了 +4 | NSFC2026我來(lái)了 2026-02-28 | 4/200 |
|
|
[碩博家園] 博士自薦 +7 | 科研狗111 2026-02-26 | 11/550 |
|
|
[考研] 化工299分求調(diào)劑 一志愿985落榜 +5 | 嘻嘻(*^ω^*) 2026-03-01 | 5/250 |
|
|
[考博] 26申博 +4 | 想申博! 2026-02-26 | 6/300 |
|
|
[考研] 290求調(diào)劑 +9 | 材料專碩調(diào)劑; 2026-02-28 | 11/550 |
|
|
[論文投稿]
Optics letters投稿被拒求助
30+3
|
luckyry 2026-02-26 | 4/200 |
|